超高温多晶氧化铝复合纤维板
该产品系采用多晶氧化铝纤维为主要原料，复配填料和粘合剂等，以吸-压结合的方式成型。与市售煅烧过的纤维制品相比，具有可加工性好、导热系数和容重低的点。其中FHB1800型纤维板和异型制品可满足1800℃，长期1700℃的使用要求，已在多座窑炉上替代进口产品使用，节能果良好，降低了使用成本。
The products are fabricated by suck-press combined method using polycrystalline alumina fiber as main starting materials, adding packing materials and binders. Compared with calcined fiber products, the products are featured with better machinability, lower thermal conductivity and volume weight. The FHB1800 fiber board and special shaped products can long term serve at 1 700 ℃ and at 1 800 ℃ of the maximum, and have been used in many kilns to substitute imported products, saving energy and cutting cost.
产品性能
Product specification
产品 Product | 超高温多晶氧化铝复合纤维板 Ultra-high temperature polycrystalline alumina fiber composite board | ||||
号 Brands | FHB1500 | FHB1600 | FHB1700 | FHB1800 | |
分类温度，℃ Classification temperature | 1500 | 1600 | 1700 | 1800 | |
使用温度，℃ Max. service temperature | 1500 | 1600 | 1700 | 1800 | |
长期使用温度（炉温），℃ Long-term service temperature (furnace temperature),℃ | ≤1400 | ≤1500 | ≤1600 | ≤1700 | |
制品容重，kg.cm-3 Volume weight | 380-400 | 400 | 400 | 500 | |
导热系数w·(m·K)-1,1200℃ Thermal conductivity | 0.15 | 0.15 | 0.155 | 0.16 | |
加热线收缩率，% Linear shrinkage on heating | 1400℃ 24h | ≤0.3 | / | / | / |
1500℃ 24h | <2 | ≤0.3 | / | / | |
1600℃ 24h | / | <2 | ≤0.3 | / | |
1700℃ 24h | / | / | <2 | ≤0.5 | |
应 用
Application
高温电炉炉衬、仪器设备加热装置的隔热及电缘材料；隧道窑、辊道窑的窑衬材料。
Used as thermal and electric insulating materials for high temperature electric furnace and heating units of equipment, and lining materials for tunnel kiln and roller kiln
产品规格： 标准规格900×600×30-80（ mm）(长 * 宽* 高)
Product specification：Standard: 900×600×30-80（ mm）
(Length * width * thickness)